SUMIKASUPER LCPÀÇ ¹°¼ºÇ¥[E6000HF Series] |
Item | Test method | Unit |
E6007LHF |
E6807LHF |
E6808LHF |
E6808UHF |
E6810LHF |
|
Filler | Glass fiber | Glass fiber /inorganic |
Glass fiber /inorganic |
Glass fiber /inorganic |
Glass fiber /inorganic |
|||
Standard molding |
°C |
350 |
340 |
350 |
350 |
350 |
||
Specific gravity | ASTM D792 | 1.65 |
1.67 |
1.70 |
1.72 |
1.82 |
||
Water absorption coefficient |
ASTM D570 | % |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
|
Mold shrinkage rate | MD |
Sumitomo Chemical method |
% |
0.20 |
0.11 |
0.17 |
0.22 |
0.13 |
TD |
% |
0.60 |
0.63 |
0.40 |
1.02 |
0.38 |
||
Tensile strength |
ASTM D638 | MPa |
157 |
134 |
130 |
100 |
105 |
|
Elongation at break | % |
5.1 |
4.5 |
4.5 |
5.0 |
4.0 |
||
Flexural strength | 23 °C |
ASTM D790 | MPa |
158 |
145 |
140 |
120 |
133 |
200 °C |
MPa |
- |
29 |
- |
- |
|||
Flexural modulus | 23 °C |
ASTM D790 | MPa |
11800 |
12100 |
12500 |
9400 |
12600 |
200 °C |
MPa |
- |
4500 |
- |
- |
|||
Izod impact strength |
6.4t notched | ASTM D256 | J/m |
- |
118 |
96 |
- |
- |
6.4t without notched |
J/m |
251 |
343 |
270 |
350 |
200 |
||
Shear strength | ASTM D732 | MPa |
- |
53 |
54 |
- |
- |
|
Poisson's ratio | ASTM D785 | - |
0.41 |
0.4 |
- |
- |
||
Rockwell hardness | ASTM D785 | R scale |
106 |
101 |
97 |
96 |
102 |
|
DTUL | ASTM D648 | °C |
269 |
270 |
270 |
240 |
266 |
|
Soldering resistance | Sumitomo Chemical method |
°C |
300 |
295 |
280 |
290 |
280 |
|
Linear expansion coefficient (150 °C) |
MD |
Sumitomo Chemical method |
10-5/% |
0.2 |
1.0 |
0.4 |
1.0 |
- |
TD |
10-5/% |
8.5 |
6.3 |
8.1 |
6.2 |
- |
||
Limiting oxygen index | JIS K7201 | 40 |
45 |
44 |
48 |
48 |
||
Flame retardancy | flame class | UL94 | mmt |
V-0 |
V-0 |
V-0 |
V-0 |
V-0 |
color | ALL |
ALL |
NC,BK |
NC,BK |
NC,BK |
|||
thickness | 0.3 |
0.3 |
0.3 |
0.3 |
0.3 |
|||
Thermal conductivity | JIS R2618 | W/mk |
- |
0.56 |
- |
- |
- |
|
kcal/mhr°C |
- |
0.48 |
- |
- |
- |
|||
Dielectric constant | (103Hz) |
ASTM D150 | - |
4.7 |
- |
- |
- |
|
(106Hz) |
3.8 |
4.1 |
3.8 |
3.8 |
4.1 |
|||
(109Hz) |
3.5 |
- |
3.6 |
3.4 |
3.8 |
|||
Dielectric tangent | (103Hz) |
- |
0.024 |
- |
- |
- |
||
(106Hz) |
0.026 |
0.03 |
0.038 |
0.033 |
0.02 |
|||
(109Hz) |
0.004 |
- |
0.004 |
0.004 |
0.004 |
|||
Specific volume resistance | ASTM D257 | Ωm |
1013 |
1013 |
1013 |
1013 |
1013 |
|
Arc resistance | ASTM D495 | sec |
124 |
180 |
140 |
132 |
181 |
|
Tracking resistance | IEC method | V |
175 |
150 |
190 |
200 |
200 |