SUMIKASUPER LCPÀÇ ¹°¼ºÇ¥[E5000 Series] |
Item | Test method | Unit |
E5008L |
E5006L |
E5008 |
E5002L |
E5204L |
|
Filler | Glass fiber | Glass fiber | Glass fiber | Glass fiber | Glass fiber /inorganic |
|||
Standard molding |
°C |
400 |
400 |
400 |
400 |
400 |
||
Specific gravity | ASTM D792 | 1.69 |
1.60 |
1.69 |
1.45 |
1.21 |
||
Water absorption coefficient |
ASTM D570 | % |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
|
Mold shrinkage rate | MD |
Sumitomo Chemical method |
% |
0.05 |
0.02 |
0.06 |
0.07 |
0.57 |
TD |
% |
0.81 |
0.86 |
1.25 |
1.27 |
1.70 |
||
Tensile strength |
ASTM D638 | MPa |
123 |
151 |
111 |
150 |
89 |
|
Elongation at break | % |
3.7 |
4.5 |
4.8 |
4.7 |
5.5 |
||
Flexural strength | 23 °C |
ASTM D790 | MPa |
127 |
152 |
127 |
127 |
93 |
200 °C |
MPa |
39 |
- |
39 |
- |
- |
||
Flexural modulus | 23 °C |
ASTM D790 | MPa |
13400 |
14200 |
12200 |
9510 |
6960 |
200 °C |
MPa |
6370 |
- |
5880 |
- |
- |
||
Izod impact strength |
6.4t notched | ASTM D256 | J/m |
49 |
109 |
88 |
175 |
- |
6.4t without notched |
J/m |
324 |
382 |
441 |
480 |
343 |
||
Shear strength | ASTM D732 | MPa |
53 |
- |
50 |
- |
- |
|
Poisson's ratio | ASTM D785 | 0.44 |
0.48 |
0.41 |
0.51 |
- |
||
Rockwell hardness | ASTM D785 | R scale |
89 |
90 |
89 |
- |
90 |
|
DTUL | ASTM D648 | °C |
339 |
355 |
335 |
354 |
351 |
|
Soldering resistance | Sumitomo Chemical method |
°C |
340 |
350 |
340 |
350 |
- |
|
Linear expansion coefficient (150 °C) |
MD |
Sumitomo Chemical method |
10-5/% |
0.2 |
1.7 |
0.1 |
0.2 |
1.3 |
TD |
10-5/% |
6.0 |
7.3 |
6.4 |
8.1 |
7.3 |
||
Limiting oxygen index | JIS K7201 | 47 |
- |
47 |
- |
- |
||
Flame retardancy | flame class | UL94 | mmt |
V-0 |
V-0 |
V-0 |
V-0 |
V-0 |
color | ALL |
ALL |
ALL |
ALL |
NC,BK |
|||
thickness | 0.3 |
0.3 |
0.3 |
0.3 |
0.29 |
|||
Thermal conductivity | JIS R2618 | W/mk |
0.56 |
0.54 |
0.56 |
0.44 |
0.38 |
|
kcal/mhr°C |
0.48 |
- |
0.48 |
- |
- |
|||
Dielectric constant | (103Hz) |
ASTM D150 | 4.7 |
- |
4.7 |
- |
- |
|
(106Hz) |
4.2 |
3.7 |
4.2 |
3.4 |
3.1 |
|||
(109Hz) |
- |
3.4 |
- |
3.1 |
2.8 |
|||
Dielectric tangent | (103Hz) |
0.013 |
- |
0.015 |
- |
- |
||
(106Hz) |
0.031 |
0.022 |
0.031 |
0.023 |
0.018 |
|||
(109Hz) |
- |
0.004 |
- |
0.004 |
0.003 |
|||
Specific volume resistance | ASTM D257 | Ωm |
1013 |
1013 |
1013 |
1014 |
1013 |
|
Arc resistance | ASTM D495 | sec |
128 |
- |
128 |
- |
- |
|
Tracking resistance | IEC method | V |
185 |
- |
175 |
- |
- |