SUMIKASUPER LCPÀÇ ¹°¼ºÇ¥[E4000 Series] |
Item | Test method | Unit |
E4008 |
E4006L |
E4205L |
|
Filler | Glass fiber | Glass fiber | Glass filler |
|||
Standard molding |
°C |
380 |
380 |
380 |
||
Specific gravity | ASTM D792 | 1.70 |
1.60 |
1.18 |
||
Water absorption coefficient |
ASTM D570 | % |
0.02 |
0.02 |
0.02 |
|
Mold shrinkage rate | MD |
Sumitomo Chemical method |
% |
0.10 |
0.11 |
0.66 |
TD |
% |
1.32 |
0.78 |
1.67 |
||
Tensile strength |
ASTM D638 | MPa |
150 |
182 |
82 |
|
Elongation at break | % |
5.0 |
5.6 |
5.0 |
||
Flexural strength | 23 °C |
ASTM D790 | MPa |
139 |
155 |
85 |
200 °C |
MPa |
39 |
47 |
- |
||
Flexural modulus | 23 °C |
ASTM D790 | MPa |
12300 |
11900 |
5600 |
200 °C |
MPa |
6300 |
5780 |
- |
||
Izod impact strength |
6.4t notched | ASTM D256 | J/m |
108 |
137 |
- |
6.4t without notched |
J/m |
520 |
461 |
309 |
||
Shear strength | ASTM D732 | MPa |
52 |
58 |
- |
|
Poisson's ratio | ASTM D785 | 0.49 |
0.48 |
- |
||
Rockwell hardness | ASTM D785 | R scale |
91 |
91 |
- |
|
DTUL | ASTM D648 | °C |
313 |
310 |
305 |
|
Soldering resistance | Sumitomo Chemical method |
°C |
330 |
335 |
- |
|
Linear expansion coefficient (150 °C) |
MD |
Sumitomo Chemical method |
10-5/% |
1.4 |
0.2 |
- |
TD |
10-5/% |
6.2 |
8.1 |
- |
||
Limiting oxygen index | JIS K7201 | 48 |
44 |
|||
Flame retardancy | flame class | UL94 | mmt |
V-0 |
V-0 |
V-0 |
color | NC,BK |
NC,BK |
BK |
|||
thickness | 0.3 |
0.3 |
0.3 |
|||
Thermal conductivity | JIS R2618 | W/mk |
0.57 |
0.53 |
0.41 |
|
kcal/mhr°C |
0.49 |
0.46 |
0.35 |
|||
Dielectric constant | (103Hz) |
ASTM D150 | 4.5 |
4.4 |
- |
|
(106Hz) |
3.9 |
3.7 |
2.9 |
|||
(109Hz) |
- |
- |
- |
|||
Dielectric tangent | (103Hz) |
0.018 |
0.018 |
- |
||
(106Hz) |
0.034 |
0.035 |
0.013 |
|||
(109Hz) |
- |
- |
- |
|||
Specific volume resistance | ASTM D257 | Ωm |
1013 |
1013 |
1013 |
|
Arc resistance | ASTM D495 | sec |
130 |
130 |
- |
|
Tracking resistance | IEC method | V |
145 |
185 |
- |